name:YXJ-132Self-adhesive polymer modified bitumen membrane
1.Product Name:YXJ-132Self-adhesive polymer modified bitumen membrane
2.Product Features:The product is applicable to the industrial and civil buildings and underground waterproofing works, especially suitable for the waterproofing of buildings at low temperature.
3.Usage:No tire base (class N) self-adhesive membrane for non-exposed waterproofing, self-adhesive membrane foil is applied to the exposed surface of the material waterproofing, membrane-sided self-adhesive waterproofing membrane applied to the auxiliary. Child-reinforced polyester (PY class) is widely used in building self-adhesive membrane roofing, basements, bridges, tunnels and other waterproof, impermeable, moisture engineering, but also for wood and steel structure roof waterproofing.
4.Product Performance:
4.1Product Specifications:
Project |
Class N |
Class PY |
Web width ,㎜ |
1000 |
1000 |
Membrane area ,㎡ |
10、 15、 20 |
10、15 |
Membrane thickness ,㎜ |
1.2、 1.5、 2.0 |
2.0、 3.0、 4.0 |
4.2 Key performance indicators (Executive GB23441-2009 standard)
4.2.1 N class self-adhesive membrane
Project |
Index |
|||||||
PE |
PET |
D |
||||||
Ⅰ |
Ⅱ |
Ⅰ |
Ⅱ |
|||||
Tensile Properties |
Tension∕(N∕50㎜) ≥ |
150 |
200 |
150 |
200 |
- |
||
Elongation at Maximum Tension∕% ≥ |
200 |
30 |
- |
|||||
Elongation at Asphalt Break∕% ≥ |
250 |
150 |
450 |
|||||
Phenomenon during Stretch |
There is no separation of asphalt coating and membrane before break. |
- |
||||||
Tear Strength by Nail Shank∕N ≥ |
60 |
110 |
30 |
40 |
- |
|||
Heat Resistance |
70℃The slide does not exceed2㎜ |
|||||||
Low Temperature Flexibility∕℃ |
-20 |
-30 |
-20 |
-30 |
-20 |
|||
No cracks |
||||||||
Waterproofness |
0.2MPa,120minWaterproofness |
- |
||||||
Peel Strength∕(N∕㎜) ≥ |
1.5(Roll and Aluminum Sheet) |
|||||||
Adhesion∕min ≥ |
20 |
4.2.2 PY class self-adhesive membrane
Project |
Index |
|||
Ⅰ |
Ⅱ |
|||
Content of Soluble Matter(g∕㎡) ≥ |
2.0㎜ |
1300 |
- |
|
3.0㎜ |
2100 |
|||
4.0㎜ |
2900 |
|||
Tensile Properties |
Tension(N∕50㎜)≥ |
2.0㎜ |
350 |
- |
3.0㎜ |
450 |
600 |
||
4.0㎜ |
450 |
800 |
||
Elongation at Maximum Tension ∕% ≥ |
30 |
40 |
||
Heat Resistance |
70℃No sliding, flowing, dripping |
|||
Waterproofness |
0.3MPa,120minImpermeable |
|||
Low Temperature Flexibility∕℃ |
-20 |
-30 |
||
No cracks |
||||
Peel Strength∕(N∕㎜) ≥ |
1.5(Roll and Aluminum Sheet) |
|||
Adhesion∕min ≥ |
15 |
|||
Self-adhesive bitumen and then peel strength∕(N∕㎜) ≥ |
1.5 |
5.Construction Points:
5.1 Construction Process: Base treatment - Detail treatment- Self-adhesive membrane paving - Sealing head treatment - Quality acceptance - Protective layer
5.2Base Requirement: The base should be flat and solid, and has no cavity or dusting. The corner should be circular arc.
5.3 Base Treatment: The base is uniformly coated with treating agent at first and the self-adhesive membrane can be paved after drying. 5.4 Construction:
①After peeling off the isolating film, the self-adhesive membrane is directly paved on the base along the bonding jumper from low to high in the horizontal plane and from bottom to top in the vertical plane.
②The rubber scraper or compression roller should be used to exhaust the air under the self-adhesive membrane and ensure tight cohesion. ③The sealing head treatment is performed after paving.
5.5The construction is performed according to Technical Code for Roof Engineering and Technical Code for Waterproofing of Underground Works.
6.Packaging, Transportation and Storage:
6.1 The self-adhesive membrane is packaged according to the requirements of transportation and storage.
6.2The products with different varieties, models and specifications should be stacked separately, and mixing is prevented. The (N) self-adhesive membrane should be put horizontally, and the stockpile height should not be more than 5 layers. The single-layer (PY) self-adhesive membrane is placed vertically. It should be stored in a ventilated place and not to be exposed to the sun and rain. The storage temperature should never be higher than
6.3 During transportation, the inclination or horizontal compression should be prevented. If necessary, it should be covered with felt-cloth.
6.4 The storage period is one year since production date under normal conditions of storage and transportation.
Shanghai Waterproof Building Materials (Group) Co., Ltd. Manufacturer: on Haijin Xia Building Materials Co., Ltd.
Address: Taihe Road, Shanghai 1400
TEL:021-64387777 021-64383623 Zip Code: 201901
Fax:021-62891692 Zip Code:200040